White EVA II  Film (SV-15297W)

White EVA II Film (SV-15297W)

常州斯威克光伏新材料有限公司
价 格:
起价 ¥11.0 / m2 *
类型: 超快固型
地区: 中国大陆 中国大陆
注意: 您的询盘将直接发送至常州斯威克光伏新材料有限公司

描述:

WHITE EVA II FILM (SV-15297W)

  • Excellent durability (including high resistance to temperature, humidity and UV)

  • Transparent EVA on the cell face and white EVA on the back

  • Can be used for G-to-G solar modules, normal solar modules and thin-film solar modules

产品特点

产品特点  
类型 超快固型
厚度 0.45-0.75 mm
卷长 100-200 m
密度 0.96 g/cm3
交联度 ≥75 %
稳定性能  
抗拉强度 18 Mpa
断裂伸长率 550 %
剥离强度(密封材料-玻璃) ≥60 N/cm
剥离强度(密封材料-背板) ≥40 N/cm
热收缩率(纵向) ≤3 %
热收缩率(横向) ≤2 %
体积电阻率 >1x10 ^15 Ω·cm
紫外老化(黄变指数) ≤2 △YI
耐湿热老化(黄变指数) ≤3 △YI
光热特性  
透光率 ≥80 %
层压工艺时间  
抽真空时间 5-6 min
层压时间 7-12 min
PDF  
下载公司产品详情

Technical Parameters

model

SV-15297W

length

100m

Width / thickness

Customized according to customer requirements

performance

project

standard test

unit

SV-15296P

SV-15297W

Physical properties

Thickness tolerance

GB/T 6672-2001

mm

+/-0.05

Width tolerance

mm

+5/-3

density

ASTM D792

g/cm3

0.96

Tensile strength (after curing)

GB/T 13022-91

Mpa

≥16

≥16

Elongation at break (after curing)

%

550

550

Glass strength of film and glass

ASTM D903

N/cm

>60

Glass strength of adhesive film and back sheet

N/cm

>40

Thermal performance

Shrinkage

ASTM 1204

MD%

<3

TD%

<2

Degree of cross-linking

ASTM D2765

%

>75

>75

Electrical performance

Transmittance

(280nm~380nm)

GB/T2410-2008

%

≥80

--

Transmittance

(400-700nm)

%

≥91

--

Reflectance

(400-700nm)

%

--

≥90

Weatherability

UV aging yellowing index

(60kWh/m2 )

ΔYI

<2

Damp heat aging

85℃/85RH 1000h

ΔYI

<3


Lamination process

model

Lamination temperature(℃)

When vacuuming(min)

Lamination time(min)

SV-15296P/SV-15297W

140-150

5-6

7-12

Note: As different customers have different lamination equipment and cross-linking requirements, this process is only our recommendation, and customers can find the process that suits them best.

Product advantage

White EVA II FILM

•No need to adjust lamination cycle, Solving the overflow and wrikle prdblem.

•Excellent durability (including high resistance for temperature, humidity and UV).

•Transparent EVA on the cell face and white EVA on the back, significantly reduce the ratio of crack during lamination and provide better bonding performance after aging.

•Easy for processing and quality stable during laminating.

•Low shrinkage rate, to make sure the stable quality during laminating.

•High reflectivity, to guarantee the maximum efficiency output of solar module.

•Can be used for G to G solar module, normal solar module and thin film solar module.


Certificates

常州斯威克光伏新材料有限公司

Click to show company phone
www.sveck.com.cn
中国大陆
江苏省常州市金坛区直溪镇直溪大道6号
员工数: 1,100
注意: 您的询盘将直接发送至常州斯威克光伏新材料有限公司

有用联系人

Contact Face
李经理
Contact Face
lyn
公司描述

Changzhou Sveck Photovoltaic New Materials Co, Ltd, formerly Shenzhen Sveck Technology Co., Ltd, was founded in 2005 and moved to Jintan District, Changzhou City, Jiangsu Province in 2010 (Changzhou base), and the Yiwu base was running into operation by the end of 2020. Sveck is an innovative enterprise engaged in the new material industry, covering an area of about 245 mu. The company has about 1100 employees and has been operating two production bases (Changzhou and Yiwu), At present, the annual production capacity has reached 480 million square meters.

产品

Jiangsu Sveck Photovoltaic New Material Co., Ltd is a company is an innovative enterprise engaged in the new material industry, aiming to become the leading brand in the new material field. Our company was founded in Shenzhen (former name: Shenzhen Sveck Tech Co., Ltd), in 2010, we moved to Jintan Changzhou district, Jiangsu province (Changzhou Base), at the end of 2020, Yiwu base was put into production, our Suqian base has started since April of 2022. All the 3 bases (Changzhou, Yiwu, and Suqian) have an annual capacity of 900 million sqm.

As a supplier of integrated solutions for the new materials industry, Sveck focuses on the integration of R&D, production and sales and kept its innovation according to the needs of our customers, and cooperated well with our allies. After 17 years of efforts indicated in encapsulation material for photovoltaic, our film was used in digital products, new energy automobiles, and also for solar modules, which achieved a lot of praise from our customers. Our core business: Anti-PID EVA film, White EVA, EPE film, POE film, EPE white film, LRF, Aluminum-plastic film etc. And we had sold our film to over 20 countries and regions.

Sveck has been in pursuit of excellence and technological innovation, our product has achieved UL, TUV, VDE, PCCC, and SGS certifications. And we have created over 20 invention patents, 89 utility model patents and 3 appearance patents, and another 99 invention patents are under examination. Sveck was awarded “New giant of national elite”, “Jiangsu postdoctoral innovation practice base”, “Quality credit AA enterprises in Jiangsu Province”, “High-tech enterprises”, “Integration of Industry & Information standard”, “Mayor Quality Award”, “Green factory” etc. The R&D team achieved “Jiangsu Photovoltaic module encapsulation materials engineering technology research centre”, “Jiangsu Enterprise technology centre” etc. Also, with “CNAS national lab” certification.

Over the years, Sveck adhere to the technology-leading, quality-oriented development path, customer-centred, service to provide value. At the same time, the company has a dedicated R&D team led by several senior engineers and doctors, perfect scientific research equipment and scientific and rigorous R&D process, and a postdoctoral innovation practice base in Jiangsu Province. Sveck is committed to creating greater value for customers and serving our customers with excellent product quality, fast delivery capacity and a perfect after-sales system.

Certificates
Exihibition

来自常州斯威克光伏新材料有限公司的其他4个系列产品

  • ¥11.0 / Wp *
    Anti PID EVA...
    超快固型
  • ¥11.0 / Wp *
    White EVA fil...
    超快固型
  • ¥11.0 / Wp *
    PO film (SE-5...
    常规型
  • ¥11.0 / Wp *
    PO II FLIM (C...
    超快固型